Fatigue failure of anterior teeth without ferrule restored with individualized fiber-reinforced post-core foundations
<p><strong>Objectives: </strong>The aim was to explore the survival of extensively damaged anterior teeth without ferrule restored with different fiber-reinforced composite (FRC) post-core foundations and composite ...
Mechanical Performance of Direct Restorative Techniques Utilizing Long Fibers for "Horizontal Splinting" to Reinforce Deep MOD Cavities-An Updated Literature Review
<p>Excessive cavity preparation and root canal treatment leads to a weakened tooth structure with a lower resistance to fracture. Fiber reinforcement is frequently used to reinforce such teeth, and multiple fiber types and ...
Fatigue failure load of immature anterior teeth: influence of different fiber post-core systems
<p>The aim was to explore the fracture-behavior, survival and marginal-microgaps within the root-canal of immature anterior teeth restored with different fiber-reinforced post-core composites (FRCs). 180 bovine-incisors were randomly divided into 6 groups (n=30). One group served as control (group 6). The rest of the teeth were prepared to an internal diameter of 1.6 mm and the apex was sectioned. After application of an MTA-plug, teeth were restored with FRC materials: Group 1: Bioblock technique with short fiber-reinforced composite (SFRC); Group 2: Bioblock technique with flowable SFRC; Group 3: Individually-made FRC post; Group 4: Conventional FRC post; Group 5: dual-cure core build-up composite. After restorations were completed, teeth (n=5/group) were sectioned and then stained. Specimens were viewed under a stereo microscope and the percentage of microgaps within the root-canal was calculated. Fatigue-survival was measured using a cyclic-loading testing machine in the rest of the specimens. Flowable SFRC application in the root-canal (Group 2) did not differ from intact-teeth regarding fatigue-survival (p>0.05). The rest of the groups produced significantly lower survival (p<0.05) compared to intact-teeth. Post/core restorations made from conventional FRC post (Group 4) exhibited a high number of microgaps (38.3%) at the examined interphase in the root-canal. The restoration of immature incisors with the use of flowable SFRC as post-core material displayed promising performance in matter of fatigue-resistance and survival.<br></p>...
Fatigue performance of endodontically treated premolars restored with direct and indirect cuspal coverage restorations utilizing fiber-reinforced cores
<p><strong>Objectives: </strong>The aim of this in vitro study was to investigate the fatigue survival and fracture behavior of endodontically treated (ET) premolars restored with different types of post-core and cuspal ...
The biomechanical effect of root amputation and degree of furcation involvement on intracoronally splinted upper molar teeth – An in vitro study
<p><strong>Objectives: </strong>The aim of this study was to evaluate the effect of the amount of periodontal support and the presence or absence of root amputation on the fracture resistance of intracoronally splinted ...
Fatigue behavior of endodontically treated premolars restored with different fiber-reinforced designs
<p><strong>Objectives: </strong>The aim was to investigate the fatigue survival and marginal-gap inside the root-canal of endodontically treated (ET) premolars reinforced by various fiber-reinforced post-core composites ...
Fracture Behavior and Integrity of Different Direct Restorative Materials to Restore Noncarious Cervical Lesions
<p>The purpose of this study was to analyze the fracture resistance and marginal leakage of noncarious cervical lesion (NCCL) restorations made of different restorative materials. Eighty upper premolars were randomly divided into four groups (n = 20/group). Standardized NCCL cavity preparations were performed on the buccal surface of the teeth and then restored with four different materials. Group 1: Packable resin composite (PC); Group 2: Highly flowable resin composite (HF); Group 3: Low flowable resin composite (LF); Group 4: Resin modified glass ionomer cement (RMGIC). After restorations were completed, cyclic and static fracture behavior was evaluated using a loading testing machine. Extra restored teeth were sectioned and then stained (n = 5/group). The specimens were viewed under a stereo microscope and the percentage of microgaps at the tooth-restoration interface was calculated. All restored teeth survived after fatigue loading. There was no statistically significant (p > 0.05) difference between the tested restorations after the static loading test. NCCLs restored with highly filled flowable composite showed the least microleakage among the tested groups (p < 0.05). The investigated restorative materials are acceptable for NCCL restorations in terms of fracture resistance and microleakage.<br></p>...
Fracture Resistance and Microleakage around Direct Restorations in High C-Factor Cavities
<p>The aim of this research was to evaluate the mechanical impact of different direct restorations in terms of fracture resistance, and subsequent fracture pattern, in occlusal high C-factor cavities. Furthermore, the adaptation of different direct restorations in the form of gap formation was also evaluated. Seventy-two intact mandibular molars were collected and randomly distributed into three groups (n = 24). Class I occlusal cavities with standardized dimensions were prepared in all specimens. After adhesive treatment, the cavities were restored with direct restorations utilizing three different materials. Group 1: layered conventional packable resin composite (Filtek Ultimate), Group 2: bulk-fill resin composite (SDR), Group 3: bulk-fill short fibre-reinforced composite (SFRC; everX Posterior) covered with packable composite occlusally. Half of the restored specimens underwent static load-to fracture testing (n = 12/group), while the rest underwent sectioning and staining for microleakage evaluation and gap formation analysis. Fracture patterns were evaluated visually among the mechanically tested specimens. The layered composite restoration (Group 1) showed significantly lower fracture resistance compared to the bulk fill groups (Group 2, p = 0.005, Group 3, p = 0.008), while there was no difference in fracture resistance between the other groups. In terms of gap formation values, the layered composite restoration (Group 1) produced significantly higher gap formation compared to the bulk-fill groups (Group 2, p = 0.000, Group 3, p = 0.000). Regarding the fracture pattern, SFRC (Group 3) produced the highest number, while SDR (Group 2) produced the lowest number of repairable fractures. The use of bulk-fill resin composite (fibre or non-fibre-reinforced) for occlusal direct restorations in high C-factor cavities showed promising achievements regarding both fracture resistance and microleakage. Furthermore, the use of short fibre-reinforced bulk-fill composite can also improve the fracture pattern of the restoration-tooth unit. Bulk-fill materials provide a simple and effective solution for restoring and reinforcing high C-factor occlusal cavities.<br></p>...
Fracture behavior of short fiber-reinforced direct restorations in large MOD cavities
<p>The aim of this research was to study the impact of using a short fiber-reinforced composite (SFRC) core on the fatigue performance and fracture behavior of direct large posterior composite restorations. Moreover, the influence of the consistency (flowable or packable) of occlusal composite coverage was assessed. A total of 100 intact molars were collected and randomly distributed into five groups (n = 20). Deep mesio-occlusal-distal (MOD) cavities were prepared in all groups. After adhesive treatment and rebuilding the missing interproximal walls with conventional composite, the specimens in four experimental groups were restored by an SFRC core (everX Flow), which was applied and cured either in bulk or in oblique layers (each 2 mm thick). Packable (G-aenial Posterior) or flowable (G-aenial Injectable) conventional composites were used as a final occlusal layer. The control group was restored with only packable conventional composite. Fatigue survival was measured for all specimens using a cyclic loading machine until a fracture occurred or a total of 25,000 cycles was achieved. Kaplan-Meyer survival analyses were conducted, followed by pairwise log-rank post hoc comparisons. The static load-bearing capacity of surviving teeth was tested using a universal testing machine. Fracture patterns were evaluated visually. There was no statistically significant (p > 0.05) difference in terms of survival between the tested groups. All groups for which flowable SFRC was used showed statistically significantly higher load-bearing capacities compared to the control group (p < 0.05). There were no significant differences regarding fracture resistance among the fiber-reinforced study groups. Regarding the fracture pattern during the survival analysis, all specimens that received SFRC showed a dominantly restorable type of fracture, while the control specimens presented a dominantly non-restorable type. The use of flowable SFRC as a reinforcing core for large MOD direct restorations showed promising achievements regarding fracture behavior.<br></p>...
Fatigue performance of endodontically treated molars restored with different dentin replacement materials
<p><strong>Objectives: </strong>The aim was to investigate the fatigue performance of endodontically treated (ET) molars restored by various dentin-replacing materials and material configurations. Moreover, the impact of ...