Effect of Fiber Reinforcement Type on the Performance of Large Posterior Restorations: A Review of In Vitro Studies
<p>To reinforce extensively prepared cavities, different types of fiber reinforcement are utilized. Polyethylene and glass fibers are the most commonly used fibers in that purpose; each type has its own advantages over the ...
Fatigue failure of anterior teeth without ferrule restored with individualized fiber-reinforced post-core foundations
<p><strong>Objectives: </strong>The aim was to explore the survival of extensively damaged anterior teeth without ferrule restored with different fiber-reinforced composite (FRC) post-core foundations and composite ...
Fracture Resistance of Anterior Crowns Reinforced by Short-Fiber Composite
<p>The aim of this study was to investigate the load-bearing capacity of anterior crowns made of different commercial particulate-filled composites (PFCs) and reinforced by a core of short-fiber composite (SFC) (bilayer ...
Fracture behavior of discontinuous fiber-reinforced composite inlay-retained fixed partial denture before and after fatigue aging
<p><strong>Purpose: </strong>To evaluate the fracture behavior of inlay-retained fixed partial dentures (IRFPDs) made of experimental short fiber-reinforced composite (SFRC) computer-aided design/computer-aided manufacturing (CAD/CAM) block before and after cyclic fatigue aging.</p><p><strong>Methods: </strong>Five groups (n=20/group) of three-unit posterior IRFPDs were fabricated. The first and second groups were CAD/CAM fabricated from experimental SFRC blocks or lithium-disilicate (IPS e.max CAD, IVOCLAR) materials, the third group comprised a three-dimensional-printed composite (Temp PRINT, GC), and the fourth and fifth groups comprised conventional laboratory flowable composite (Gradia Plus, GC) and commercial flowable SFRC (everX Flow, GC), respectively. All IRFPDs were luted into a metal jig with adhesive dual-cure resin cement (RelyX Ultimate, 3M ESPE). Half the IRFPDs per group (n=10) were subjected to fatigue aging for 10,000 cycles. The remaining half were statically loaded until fracture without fatigue aging. The load was applied vertically between triangular ridges of the buccal and lingual cusps. The fracture mode was visually examined using optical and scanning electron microscopy (SEM). Data were statistically analyzed using a two-way analysis of variance (ANOVA) followed by Tukey's HSD test.</p><p><strong>Results: </strong>ANOVA revealed that IRFPDs made of experimental SFRC CAD/CAM had the highest (p<0.05) load-bearing capacity before (2624±463 N) and after (2775±297 N) aging among all groups. Cyclic fatigue aging decreased the load-bearing capacity (p>0.05) of all tested prostheses, except for the experimental SFRC CAD/CAM and conventional laboratory composite IRFPDs (p>0.05). SEM images showed the ability of discontinuous short fibers in the experimental SFRC CAD/CAM composite to redirect and hinder crack propagation.</p><p><strong>Conclusion: </strong>CAD/CAM-fabricated IRFPDs made of experimental SFRC blocks showed promising performance in clinical testing in terms of fracture behavior.</p>...
Effect of Accelerated Aging on Some Mechanical Properties and Wear of Different Commercial Dental Resin Composites
<p>The aim of current in vitro research was to determine the effect of hydrothermal accelerated aging on the mechanical properties and wear of different commercial dental resin composites (RCs). In addition, the effect of ...
Fatigue failure load of immature anterior teeth: influence of different fiber post-core systems
<p>The aim was to explore the fracture-behavior, survival and marginal-microgaps within the root-canal of immature anterior teeth restored with different fiber-reinforced post-core composites (FRCs). 180 bovine-incisors were randomly divided into 6 groups (n=30). One group served as control (group 6). The rest of the teeth were prepared to an internal diameter of 1.6 mm and the apex was sectioned. After application of an MTA-plug, teeth were restored with FRC materials: Group 1: Bioblock technique with short fiber-reinforced composite (SFRC); Group 2: Bioblock technique with flowable SFRC; Group 3: Individually-made FRC post; Group 4: Conventional FRC post; Group 5: dual-cure core build-up composite. After restorations were completed, teeth (n=5/group) were sectioned and then stained. Specimens were viewed under a stereo microscope and the percentage of microgaps within the root-canal was calculated. Fatigue-survival was measured using a cyclic-loading testing machine in the rest of the specimens. Flowable SFRC application in the root-canal (Group 2) did not differ from intact-teeth regarding fatigue-survival (p>0.05). The rest of the groups produced significantly lower survival (p<0.05) compared to intact-teeth. Post/core restorations made from conventional FRC post (Group 4) exhibited a high number of microgaps (38.3%) at the examined interphase in the root-canal. The restoration of immature incisors with the use of flowable SFRC as post-core material displayed promising performance in matter of fatigue-resistance and survival.<br></p>...
Fatigue performance of endodontically treated premolars restored with direct and indirect cuspal coverage restorations utilizing fiber-reinforced cores
<p><strong>Objectives: </strong>The aim of this in vitro study was to investigate the fatigue survival and fracture behavior of endodontically treated (ET) premolars restored with different types of post-core and cuspal ...
Shear-bond strength and optical properties of short fiber-reinforced CAD/CAM composite blocks
<p>The aim of this study was to assess the shear-bond strength (SBS) of resin-luting cement to experimental short fiber-reinforced CAD/CAM composite (SFRC) compared to conventional CAD/CAM (Cerasmart 270), 3D printed (GC ...
Development and characterization of ion-releasing fiber-reinforced flowable composite
<p><strong>Objective: </strong>This study aimed to develop and characterize an ion-releasing experimental fiber-reinforced flowable composite (Bio-SFRC) and dentin treatment solution made of poly(acrylic acid) (PAA) with ...
Fatigue behavior of endodontically treated premolars restored with different fiber-reinforced designs
<p><strong>Objectives: </strong>The aim was to investigate the fatigue survival and marginal-gap inside the root-canal of endodontically treated (ET) premolars reinforced by various fiber-reinforced post-core composites ...