Optimisation of trabecular bone mimicking silicon-hydroxyapatite based composite scaffolds processed through selective laser melting

Kamboj Nikhil; Ivanković Hrovoje; Hussainova Irina; Ressler Antonia

Optimisation of trabecular bone mimicking silicon-hydroxyapatite based composite scaffolds processed through selective laser melting

Kamboj Nikhil
Ivanković Hrovoje
Hussainova Irina
Ressler Antonia
Katso/Avaa
KambojEtAl2022OptimisationOfTrabecularBone.pdf (10.06Mb)
Lataukset: 

Elsevier B.V.
doi:10.1016/j.oceram.2022.100252
URI
https://doi.org/10.1016/j.oceram.2022.100252
Näytä kaikki kuvailutiedot
Julkaisun pysyvä osoite on:
https://urn.fi/URN:NBN:fi-fe2022081154625
Tiivistelmä

Additive manufacturing is a rapid prototyping technology to produce complex three-dimensional scaffolds suitable for personalized medicine. In the present study, the laser powder bed fusion through a selective laser melting (SLM) approach has been applied to optimized fabrication of bio-mimicking scaffolds by using hydroxyapatite (HAp, 50 and 70 wt%) and silicon powder mixture. In situ formation of pseudo-wollastonite (P–W, CaSiO3) has been detected along with silicon for 50 wt% of HAp powder mixture, while an increase in HAp content has resulted in P–W, silicon and larnite (Ca2SiO4) formation. The pore size of 400 μm, according to the CAD model, are observed at the scaffolds fabricated at the shortest exposure time (50 μs), lowest laser current (500 mA) and energy density (41.6 J/mm3), and simultaneously at the highest scanning speed. Compressive stress demonstrated by the fabricated scaffolds is shown to be acceptable for their use in metaphyseal region of long bones.

Kokoelmat
  • Rinnakkaistallenteet [19207]

Turun yliopiston kirjasto | Turun yliopisto
julkaisut@utu.fi | Tietosuoja | Saavutettavuusseloste
 

 

Tämä kokoelma

JulkaisuajatTekijätNimekkeetAsiasanatTiedekuntaLaitosOppiaineYhteisöt ja kokoelmat

Omat tiedot

Kirjaudu sisäänRekisteröidy

Turun yliopiston kirjasto | Turun yliopisto
julkaisut@utu.fi | Tietosuoja | Saavutettavuusseloste